Extremely small diffusion constant of Cs in multiwalled carbon nanotubes (Articolo in rivista)

Type
Label
  • Extremely small diffusion constant of Cs in multiwalled carbon nanotubes (Articolo in rivista) (literal)
Anno
  • 2002-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1063/1.1525401 (literal)
Alternative label
  • Suzuki, S (Suzuki, S); Watanabe, Y (Watanabe, Y); Ogino, T (Ogino, T); Heun, S (Heun, S); Gregoratti, L (Gregoratti, L); Barinov, A (Barinov, A); Kaulich, B (Kaulich, B); Kiskinova, M (Kiskinova, M); Zhu, W (Zhu, W); Bower, C (Bower, C); Zhou, O (Zhou, O) (2002)
    Extremely small diffusion constant of Cs in multiwalled carbon nanotubes
    in Journal of applied physics
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Suzuki, S (Suzuki, S); Watanabe, Y (Watanabe, Y); Ogino, T (Ogino, T); Heun, S (Heun, S); Gregoratti, L (Gregoratti, L); Barinov, A (Barinov, A); Kaulich, B (Kaulich, B); Kiskinova, M (Kiskinova, M); Zhu, W (Zhu, W); Bower, C (Bower, C); Zhou, O (Zhou, O) (literal)
Pagina inizio
  • 7527 (literal)
Pagina fine
  • 7531 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 92 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
  • 12 (literal)
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • [ 1 ] NTT Basic Res Labs, Kanagawa 2430198, Japan [ 2 ] Sincrotrone Trieste, I-34012 Trieste, Italy [ 3 ] Bell Labs, Lucent Technol, Murray Hill, NJ 07974 USA [ 4 ] Univ N Carolina, Dept Phys & Astron, Chapel Hill, NC 27599 USA [ 5 ] Univ N Carolina, Curriculum Appl & Mat Sci, Chapel Hill, NC 27599 USA (literal)
Titolo
  • Extremely small diffusion constant of Cs in multiwalled carbon nanotubes (literal)
Abstract
  • The Cs intercalation process in multiwalled carbon nanotubes (MWNTs) was studied by cross-sectional scanning photoemission microscopy. Cs atoms initially deposited on the tips of aligned nanotubes diffused toward their roots. The Cs diffusion constant for the MWNTs at room temperature was evaluated from the Cs distribution measured along the axes of the tubes. The value of 2x10(-12) cm(2)/s obtained is seven orders of magnitude smaller than that in graphite, although the local atomic structure of an intercalated MWNT is very similar to that of intercalated graphite. (literal)
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Autore CNR di
Prodotto
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Insieme di parole chiave di
data.CNR.it