A thermodynamic approach to obtaining transparent spinel (MgAl2O4) by hot pressing (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• A thermodynamic approach to obtaining transparent spinel (MgAl2O4) by hot pressing (Articolo in rivista) (literal)

Anno

• 2015-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.jeurceramsoc.2014.09.005 (literal)

Alternative label

• Esposito, Laura; Piancastelli, Andreana; Miceli, Patrizia; Martelli, Stefano (2015)
  A thermodynamic approach to obtaining transparent spinel (MgAl2O4) by hot pressing
  in Journal of the European Ceramic Society
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Esposito, Laura; Piancastelli, Andreana; Miceli, Patrizia; Martelli, Stefano (literal)

Pagina inizio

• 651 (literal)

Pagina fine

• 661 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 35 (literal)

Rivista

• Journal of the European Ceramic Society (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 11 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 2 (literal)

Note

• ISI Web of Science (WOS) (literal)
• Scopus (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Consiglio Nazionale delle Ricerche (CNR); CSM Centro Sviluppo Materiali SpA (literal)

Titolo

• A thermodynamic approach to obtaining transparent spinel (MgAl2O4) by hot pressing (literal)

Abstract

• Hot pressing has been investigated as a method for producing highly transparent, cost-effective MgAl2O4 for optical applications. The hot pressing of stoichiometric Al2O3MgO powder mixtures has been preferred to the direct pressing of spinel powders, given the ready availability of pure powders and the opportunity to exploit the thermodynamic driving force for spinel formation. Ultra-pure LiF has been used as a sintering additive. An accurate thermodynamic study on the reactions involved in spinel formation has shed light on the mechanisms affecting the material's transparency, particularly as concerns the presence of a carbonaceous environment. Transparencies up to 70% in the visible range (maximum 78%) have been obtained. The present study focused on the pressure applied during sintering as one of the main parameters influencing the material's final optical properties. (C) 2014 Elsevier Ltd. All rights reserved. (literal)

Prodotto di

• Materiali ceramici trasparenti per applicazioni ottiche ed elettromagnetiche (PM.P02.020.003) (Modulo)
• Materiali ceramici trasparenti per applicazioni ottiche ed elettromagnetiche (SP.P01.033.003) (Modulo)
• Institute of science and technology for ceramics (ISTEC) (Istituto)

Autore CNR

• ANDREANA PIANCASTELLI (Unità di personale interno)
• LAURA ESPOSITO (Unità di personale interno)

Insieme di parole chiave

• Parole chiave di "A thermodynamic approach to obtaining transparent spinel (MgAl2O4) by hot pressing" (Insieme di parole chiave)

Incoming links:

Prodotto

• Institute of science and technology for ceramics (ISTEC) (Istituto)
• Materiali ceramici trasparenti per applicazioni ottiche ed elettromagnetiche (SP.P01.033.003) (Modulo)
• Materiali ceramici trasparenti per applicazioni ottiche ed elettromagnetiche (PM.P02.020.003) (Modulo)

Autore CNR di

• LAURA ESPOSITO (Unità di personale interno)
• ANDREANA PIANCASTELLI (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of the European Ceramic Society (Rivista)

Insieme di parole chiave di

• Parole chiave di "A thermodynamic approach to obtaining transparent spinel (MgAl2O4) by hot pressing" (Insieme di parole chiave)