Instrumented Indentation of Alumina-Alumina/Zirconia Multolayered Composites with residual stresses (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Instrumented Indentation of Alumina-Alumina/Zirconia Multolayered Composites with residual stresses (Articolo in rivista) (literal)

Anno

• 2006-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1080/14786430600681621 (literal)

Alternative label

• E. Jiménez-Piqué, L. Ceseracciu, Y. Gaillard, M. Brach, G. De Portu, M. Anglada (2006)
  Instrumented Indentation of Alumina-Alumina/Zirconia Multolayered Composites with residual stresses
  in Philosophical magazine (2003, Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• E. Jiménez-Piqué, L. Ceseracciu, Y. Gaillard, M. Brach, G. De Portu, M. Anglada (literal)

Pagina inizio

• 5371 (literal)

Pagina fine

• 5382 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 86 (literal)

Rivista

• Philosophical magazine (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 33-35 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• E. Jiménez-Piqué, L. Ceseracciu, Y. Gaillard, M. Anglada, Universitat Politécnica de Catalunya; M. Brach, G. De Portu, ISTEC CNR (literal)

Titolo

• Instrumented Indentation of Alumina-Alumina/Zirconia Multolayered Composites with residual stresses (literal)

Abstract

• The instrumented indentation response of polycrystalline alumina and alumina-based ceramic multilayers with well-known residual stresses is investigated. Young's modulus and hardness were evaluated as a function of penetration depth with Berkovich and spherical indenters by continuous stiffness measurements. A size effect was observed due to the length scale of the microstructure. Values of hardness and Young's modulus were in good agreement with previous works. No significant differences in the P - h curves were observed for materials with and without residual stress, making it difficult to employ the various methodologies in the literature for estimation of residual stress or crack length evaluation. Crack length had, therefore, to be measured by direct observation. Thus, cube corner indentations did not produce well-developed radial cracks but chipping of the material, whereas indentations with Berkovich indenters produced radial cracks suitable for apparent fracture toughness estimation and, consequently, residual stress (literal)

Prodotto di

• Ceramici per applicazioni strutturali e funzionali: ossidi e compositi multilaminati (SP.P08.010.001) (Modulo)
• Institute of science and technology for ceramics (ISTEC) (Istituto)

Autore CNR

• GOFFREDO DE PORTU (Persona)

Insieme di parole chiave

• Keywords of "Instrumented Indentation of Alumina-Alumina/Zirconia Multolayered Composites with residual stresses" (Insieme di parole chiave)

Incoming links:

Prodotto

• Institute of science and technology for ceramics (ISTEC) (Istituto)
• Ceramici per applicazioni strutturali e funzionali: ossidi e compositi multilaminati (SP.P08.010.001) (Modulo)

Autore CNR di

• GOFFREDO DE PORTU (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Philosophical magazine (Rivista)

Insieme di parole chiave di

• Keywords of "Instrumented Indentation of Alumina-Alumina/Zirconia Multolayered Composites with residual stresses" (Insieme di parole chiave)