Synthesis and characterization of nanophasic LaCoO3 powders (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Synthesis and characterization of nanophasic LaCoO3 powders (Articolo in rivista) (literal)

Anno

• 2002-01-01T00:00:00+01:00 (literal)

Alternative label

• L. Armelao, G. Bandoli, D. Barreca, M. Bettinelli, G. Bottaro, A. Caneschi (2002)
  Synthesis and characterization of nanophasic LaCoO3 powders
  in SIA. Surface and interface analysis
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• L. Armelao, G. Bandoli, D. Barreca, M. Bettinelli, G. Bottaro, A. Caneschi (literal)

Pagina inizio

• 112 (literal)

Pagina fine

• 115 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 34 (literal)

Rivista

• SIA. Surface and interface analysis (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 4 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• 1,3: CNR-ISTM and INSTM, Dipartimento CIMA, Università di Padova, Padova, Italy 2: Dipartimento di Scienze Farmaceutiche, Università di Padova, Padova, Italy 4: Dipartimento Scientifico e Tecnologico, Università di Verona, Verona, Italy 5: Dipartimento CIMA and INSTM, Università di Padova, Padova, Italy 6: Dipartimento di Chimica and INSTM, Università di Firenze, Firenze, Italy (literal)

Titolo

• Synthesis and characterization of nanophasic LaCoO3 powders (literal)

Abstract

• Nanophasic LaCoO3 powders were synthesized from inorganic compounds both in molten chloride fluxes and by using a solution combustion synthesis procedure. The samples were prepared in air and underwent subsequent heat treatments in order to yield the perovskite crystalline phase. The composition and microstructure of the samples were investigated by XPS, x-ray-induced AES, x-ray diffraction and electron paramagnetic resonance. Further informationwas gained by magnetic measurements. Nanophasic LaCoO3 powders with an average crystallite size of 35 nm were obtained. (literal)

Prodotto di

• Istituto di scienze e tecnologie molecolari (ISTM) (Istituto)

Autore CNR

• GREGORIO BOTTARO (Unità di personale interno)
• LIDIA ARMELAO (Unità di personale interno)
• DAVIDE BARRECA (Persona)

Insieme di parole chiave

• Parole chiave di "Synthesis and characterization of nanophasic LaCoO3 powders" (Insieme di parole chiave)

Incoming links:

Prodotto

• Istituto di scienze e tecnologie molecolari (ISTM) (Istituto)

Autore CNR di

• DAVIDE BARRECA (Persona)
• LIDIA ARMELAO (Unità di personale interno)
• GREGORIO BOTTARO (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• SIA. Surface and interface analysis (Rivista)

Insieme di parole chiave di

• Parole chiave di "Synthesis and characterization of nanophasic LaCoO3 powders" (Insieme di parole chiave)